In StockProduct: Copper Foam Structures
Copper Foam Open Cell
Copper Metal Foams
| Stock No. | NCZFF101 |
| PPI | 5-120, customization is also possible |
| Bulk Density | 0.80-0.85 g/cc |
| Purity | ≥ 99.8% |
| Porosity | ≥ 70%, customization is also possible |
| Dimension | 500mm X 500mm, customization is also possible |
| Thickness | 1mm, customization is also possible |
Physical Characteristics of heat absorbing Copper Foam
| Compression Strength | 131 psi |
| Tensile Strength | 1000 psi |
| Shear Strength | 190 psi |
| Modulus of Elasticity (Compression) | 107 kpsi |
| Modulus of Elasticity (Tension) | 14.6 × 103 psi |
| Shear Modulus | 40.9 kpsi |
| Vickers Hardness | 35 |
| Specific Heat | 0.385 J/g-°C |
| Bulk Thermal Conductivity | 10.1 W/m-°C |
| Coefficient of Thermal Expansion | 1.7 × 10-5 m/m–°C (0-100°C) |
| Bulk Resistivity | 2.56× 10-5 ohm – in |
| Melting Point | 1080 °C |
Description
Note: For pricing & ordering information, please contact us at sales@nanochemazone.com
Please contact us for quotes on Larger Quantities & Customization. E-mail: contact@nanochemazone.com
Customization:
If you are planning to order large quantities for your industrial and academic needs, please note that customization of parameters (such as size, length, purity, functionalities etc.) are available upon request.
Related Products
-
Product: Copper Foam (Cu Foam, Purity: 99.9%, 50PPI/1mm)
Copper Metal Foams
Stock No. NCZFF102 PPI 50, customization is also possible Bulk Density 0.80-0.85 g/cc Purity ≥99.9% Porosity ≥70% , customization is also possible Dimension 500mm X 500 mm, customization is also possible Thickness 1mm, customization is also possible Physical Characteristics of Cu Foam
Compression Strength 131 psi Tensile Strength 1000 psi Shear Strength 190 psi Modulus of Elasticity (Compression) 107 kpsi Modulus of Elasticity (Tension) 14.6 × 103 psi Shear Modulus 40.9 kpsi Vickers Hardness 35 Specific Heat 0.385 J/g-°C Bulk Thermal Conductivity 10.1 W/m-°C Coefficient of Thermal Expansion 1.7 × 10-5 m/m–°C (0-100°C) Bulk Resistivity 2.56× 10-5 ohm – in Melting Point 1080 °C Copper foam available as open cell and closed cell. Please ask for customization while ordering.
$0.00 -
Reticulated Vitreous Carbon Foam /Glassy Carbon Foam
open cell carbon foam
Reticulated Vitreous Carbon Foam
Product Carbon Foam (Purity: 99.9%, Thickness: 5mm)
Materials Carbon Foam Stock No NCZFF112 CAS 7440-44-0 Purity 99.9% Thickness 5 mm, customization is also possible Compression Strength 15-75 psi Tensile Strength 25-50 psi Shear Strength 4.4×103 psi Hardness 6-7 Mohs Specific Heat 0.3 BTU/lb °F Shear Modulus 4.4 × 103 psi Bulk Thermal Conductivity 0.021-0.29 BTU/ft •hr•°F Coefficient of Thermal Expansion 1.2 × 10-6 in/in°F (0-100°C) Bulk Resistivity 12.7 × 10-2 ohm • in Temperature In air 600°F Limitations Inert environment 6330°F Pore Sizes 0.040″, customization is also possible Application: Reticulated Vitreous Carbon Foam for Electrochemistry Electrodes, High Surface Area, Temperature Stability, etc.
RVC foam density is customizable on request while ordering.
$0.00 -
Aluminum Metal Foams
Product Name Aluminum Foam Stock No. NCZFF114 CAS 7429-90-5 Purity 99.9% Dimension 100mm×100mm, customization is also possible Thickness 5mm, customization is also possible Pore size 2-11mm, customization is also possible Molecular Formula Al Molecular Weight 26.98g/mol Density 0.1~0.35 g/cm³ Porosity 60-90%, customization is also possible Compressive Strength 44Mpa Bending Strength 27Mpa Acoustic absorptive 0.48 Tensile Strength 1.24 MPa Shear Strength 1.31 MPa Modulus of Elasticity (Compression) 103.08 MPa Modulus of Elasticity (Tension) 101.84 MPa Shear Modulus 199.95 MPa Vickers Pyramid Number 35 HV Specific Heat .895 J/g-C Bulk Thermal Conductivity 5.8 W/m-C Bulk Resistivity 2.84 × 10-5 ohm – in $0.00 -
Open Cell Copper Foam Heat Exchanger
Copper Metal Foam open cell
Stock No. NCZFF105 PPI 50, customization is also possible Bulk Density 0.80-0.85 g/cc Purity ≥99.9% Porosity ≥70%, customization is also possible Dimension 500mm X 500mm, customization is also possible Thickness 3mm, customization is also possible Compression Strength 131 psi Tensile Strength 1000 psi Shear Strength 190 psi Modulus of Elasticity (Compression) 107 kpsi Modulus of Elasticity (Tension) 14.6 × 103 psi Shear Modulus 40.9 kpsi Vickers Hardness 35 Specific Heat 0.385 J/g-°C Bulk Thermal Conductivity 10.1 W/m-°C Coefficient of Thermal Expansion 1.7 × 10-5 m/m–°C (0-100°C) Bulk Resistivity 2.56× 10-5 ohm – in Melting Point 1080 °C $0.00 -
Aluminium Metal Foams
Product: Aluminium Metal Foam (Closed Cell, 2-11 mm)
Stock No. NCZFF108 Density 0.1 to 0.35 g/cm³ Pore Size 2-11 mm, 5 mm (Closed Cell) Porosity 60-90%, customization is also possible Compressive Strength 44 Mpa Blending Strength 27 Mpa Acoustic Absorptive 0.48 Foam Size 100 x 100 x 5 mm, customization is also possible Physical Characteristics Aluminium Metal Foam
Heat Resistivity 660 °C Acoustic Frequency Between 125 and 2000 HZ Noise Reduction Coefficient >0.4 Thermal Insulation Properties About 1 / 400 of metal Aluminium Electromagnetic Wave Frequency Between 2.6 and 18 GHZ Electromagnetic Shielding Property Up to 60 – 90 dB Resistivity 100 Times Over Metal Aluminium $0.00 -
RVC foam density
Reticulated Vitreous Carbon Foam (RVC) / Glassy Carbon Foam
Materials Reticulated Vitreous Carbon Foam Stock No NCZFF112 CAS 7440-44-0 Purity 99.9% Thickness 5 mm-50 mm PPI 10-90 PPI $0.00